Product characteristics

23 ℃ drying time (hour)
density (g/cm³)
volume solids content (%)
color
23 ℃ coating interval (hour)
mass solid content (%)
colors
nonvolatile content (%)
magnetic content (%)
density at 25℃ (g/cm³)
theoretical coating rate (m²/ kg) (with 60um dry film)
particle size distribution >150um (%)
particle size distribution >250um (%)
component a (kg/ barrel)
21
18
33
component b (kg/ barrel)
3
2
application period (23 ℃)(23 ℃)
4
surface resistance (Ω)
curing time at 230℃ (min)
gelpectization time at 200℃ (s)
cure time at 23 ℃(minutes):
10
15
SLH06 epoxy zinc-rich primer

1 sku

SLH06 epoxy zinc-rich primer

Technical parameters

1. Color: Gray;
2. Density: about 2.6g/ cm³;
3. volume solid content: 52%;
4. Mass solid content: 88%;
5. Theoretical spreading rate: 2.5m²/kg (with 80um DFT);
6. Drying time (23 ℃): Tack free time ≤ 1 hour; Practical drying time ≤ 24 hours. full cure: 7 days;
7. Over coating Interval (23 ℃): 8 hours - 7 days (used as anticorrosive paint);
8. Product packaging: 33kg/ barrel for component A.and 2kg/ barrel for component B;
9. mass mixing ratio: A : B = 33: 2;
10. Cure time (23 ℃): 15 minutes;
11. Application period (23 ℃): 4 hours;

Executive standard

GB/T6747-2008 HG/T3668-2009

Supply capability

Brand : SHENGFANG

Guarantee period : 12 months after date of delivery

Enquiry Now
SLH100 free solvent epoxy heavy duty anti-corrosion green paint

1 sku

SLH100 free solvent epoxy heavy duty anti-corrosion green paint

Technical parameters

1. Color: Green;
2. Density: about 1.45g/ cm³;
3. volume solid content: ≥97% (mixture);
4. quality solid content: 99%;
5. Theoretical spreading rate: 2.7m²/kg (with 250um DFT);
6. Drying time (23 ℃): Tack free time ≤ 4 hours; Practical drying time ≤ 24 hours. full cure: 7 days;
7. Over coating Interval (23 ℃): 8 hours - 7 days;
8. Product packaging: the component A is 20 kg/ barrel. the component B is 4 kg/ barrel. or the component A is 25 kg/ barrel. and the component B is 10 kg/ barrel;
9. mass mixing ratio: A : B = 5:1 or 2.5:1;
10. mass mixing ratio: A : B = 3.3:1 or 2:1;
11. Cure time (23 ℃): none
12. Application period (23 ℃): 1 hours;

Executive standard

GB/T6748-2008 Q/0500SFF013-2014

Supply capability

Brand : SHENGFANG

Guarantee period : 12 months after date of delivery

Enquiry Now
SLH100 free solvent epoxy heavy duty anti-corrosion black paint

1 sku

SLH100 free solvent epoxy heavy duty anti-corrosion black paint

Technical parameters

1. Color: black;
2. Density: about 1.45g/ cm³;
3. volume solid content: ≥97% (mixture);
4. quality solid content: 99%;
5. Theoretical spreading rate: 2.7m²/kg (with 250um DFT);
6. Drying time (23 ℃): Tack free time ≤ 4 hours; Practical drying time ≤ 24 hours. full cure: 7 days;
7. Over coating Interval (23 ℃): 8 hours - 7 days;
8. Product packaging: the component A is 20 kg/ barrel. the component B is 4 kg/ barrel. or the component A is 25 kg/ barrel. and the component B is 10 kg/ barrel;
9. mass mixing ratio: A : B = 5:1 or 2.5:1;
10. mass mixing ratio: A : B = 3.3:1 or 2:1;
11. Cure time (23 ℃): none
12. Application period (23 ℃): 1 hours;

Executive standard

GB/T6748-2008 Q/0500SFF013-2014

Supply capability

Brand : SHENGFANG

Guarantee period : 12 months after date of delivery

Enquiry Now
SLH42 wear resistant epoxy blue paint

1 sku

SLH42 wear resistant epoxy blue paint

Technical parameters

1. Color: Blue;
2. Density: about 1.4g/ cm³;
3. Volume solid content: 60%;
4. Mass solid content: 80%;
5. Theoretical spreading rate: 2.9m²/kg (with 150um DFT);
6. Drying time (23 ℃): Tack free time ≤ 4 hours; Practical drying time ≤ 24 hours. full cure: 7 days;
7. Over coating Interval (23 ℃): 8 hours - 7 days;
8. Storage(Keep in a cool. dry place): at least 12 months;
9. Product packaging: 21kg/ barrel for component A.and 3kg/ barrel for component B;
10. mass mixing ratio: A : B = 7: 1;
11. Cure time (23 ℃): 10 minutes;
12. Application period (23 ℃): 4 hours;

Executive standard

GB/T9261-2008

Supply capability

Brand : SHENGFANG

Guarantee period : 12 months after date of delivery

Enquiry Now
SLH87 epoxy anticorrosive brown paint

1 sku

SLH87 epoxy anticorrosive brown paint

Technical parameters

1. Color: SLH87-1 iron red (primer);
2. Density: about 1.4g/ cm³;
3. Volume solid content: 58%;
4. Quality solid content: 76%;
5. Theoretical spreading rate: 4.1m²/kg;
SLH87-2 (finish paint) brown;
2. Density: about 1.4g/ cm³;
3. Volume solid content: 58%;
4. Quality solid content: 76%;
5. Theoretical spreading rate: 4.1m²/kg (with at least 100um DFT);
1. Drying time (23 ℃): Tack free time ≤ 4 hours; Practical drying time ≤ 24 hours. full cure: 7 days;
2. Over coating Interval (23 ℃): 8 hours - 7 days;
3. Storage(Keep in a cool. dry place): at least 12 months;
4. Product packaging: 21kg/ barrel for component A.and 3kg/ barrel for component B;
5. mass mixing ratio: A : B = 7: 1;
6. Cure time (23 ℃): 10 minutes;
7. Application period (23 ℃): 4 hours;

Executive standard

Q/0500SFF005-2014

Supply capability

Brand : SHENGFANG

Guarantee period : 12 months after date of delivery

Enquiry Now
SLWF53 fluorocarbon heavy duty anti-corrosion blue paint

1 sku

SLWF53 fluorocarbon heavy duty anti-corrosion blue paint

Technical parameters

1. Color: blue;
2. Density: about 1.2/ cm³;
3. volume solid content: 40%;
4. mass solid content: 72%;
5. Theoretical spreading rate: 8.3m²/kg (with 40um DFT);
6. Drying time (23 ℃): Tack free time ≤ 4 hour; Practical drying time ≤ 24 hours;
7.Over coating Interval (23 ℃): 6 hours - 7 days;
8. Product packaging: 18kg/ barrel for component A,and 3kg/ barrel for component B;
9. mass mixing ratio: A : B = 6: 1;
10. Cure time (23 ℃): 10 minutes;
11. Application period (23 ℃): 4 hours;

Executive standard

GB/T6745-2008 HG/T3792-2005

Supply capability

Brand : SHENGFANG

Guarantee period : 12 months after date of delivery

Enquiry Now
SLX53 high chlorinated polyethylene rustproof red paint

1 sku

SLX53 high chlorinated polyethylene rustproof red paint

Technical parameters

1, Color: red for finish paint, iron oxide red for prime paint;
2. Density: about 1.3g/ cm³;
3. volume solid content: 41%;
4.mass solid content: 70%;
5. Theoretical spreading rate: 5.2m²/ kg (with 60um DFT);
6. Drying time (23 ℃): Tack free time ≤ 1 hour; Practical drying time ≤ 8 hours;
7. Over coating Interval (23 ℃): at least 8 hours;

Executive standard

HG/T4338-2012 Q/0500SFF006-2014

Supply capability

Brand : SHENGFANG

Guarantee period : 12 months after date of delivery

Enquiry Now
SLX53  high chlorinated  polyethylene rustproof  blue paint

1 sku

SLX53 high chlorinated polyethylene rustproof blue paint

Technical parameters

1. Color: blue for finish paint, iron oxide red for prime paint;
2. Density: about 1.3g/ cm³;
3. volume solid content: 41%;
4.mass solid content: 70%;
5. Theoretical spreading rate: 5.2m²/ kg (with 60um DFT);
6. Drying time (23 ℃): Tack free time ≤ 1 hour; Practical drying time ≤ 8 hours;
7. Over coating Interval (23 ℃): at least 8 hours;

Executive standard

HG/T4338-2012 Q/0500SFF006-2014

Supply capability

Brand : SHENGFANG

Guarantee period : 12 months after date of delivery

Enquiry Now
SLE01 single-layer fusion bonded epoxy powder paint (white)

1 sku

SLE01 single-layer fusion bonded epoxy powder paint (white)

Technical parameters

1. Color: White;
2. Density (25℃): About 1.42g/cm³;
3. Nonvolatile content ≥ 99.5%;
4. Magnetic content <0.002%;
5. Gelpectization time (230℃) 8~30s usually about 12s;
6. Curing time (230℃) ≤ 1.5min;
7. Particle size distribution >150um, 0.62%; > 250um, 0.03%;

Executive standard

SY/T0315-2013

Supply capability

Brand : SHENGFANG

Guarantee period : 12 months since cargo delivery date from storage

Enquiry Now
SLH87 epoxy anticorrosive black paint

1 sku

SLH87 epoxy anticorrosive black paint

Technical parameters

1. Color: SLH87-1 iron red (primer);
2. Density: about 1.4g/ cm³;
3. Volume solid content: 58%;
4. Quality solid content: 76%;
5. Theoretical spreading rate: 4.1m²/kg;
SLH87-2 (finish paint) black;
2. Density: about 1.4g/ cm³;
3. Volume solid content: 58%;
4. Quality solid content: 76%;
5. Theoretical spreading rate: 4.1m²/kg (with at least 100um DFT);
1. Drying time (23 ℃): Tack free time ≤ 4 hours; Practical drying time ≤ 24 hours. full cure: 7 days;
2. Over coating Interval (23 ℃): 8 hours - 7 days;
3. Storage(Keep in a cool. dry place): at least 12 months;
4. Product packaging: 21kg/ barrel for component A.and 3kg/ barrel for component B;
5. mass mixing ratio: A : B = 7: 1;
6. Cure time (23 ℃): 10 minutes;
7. Application period (23 ℃): 4 hours;

Executive standard

Q/0500SFF005-2014

Supply capability

Brand : SHENGFANG

Guarantee period : 12 months after date of delivery

Enquiry Now